ASTM A516 Grade 65
ASTM A516 Grade 65 is an excellent weldable carbon steel choice for pressure vessels and boiler fabrication. The material offers excellent performance in lower than ambient temperature service, has good weldability and excellent notch toughness.
A516 Grade 65 has greater specified tensile and yield strength when compared with ASTM A516 Grade 60
Used throughout the oil, gas and petrochemical industry, the steel is also found in sour service and wet H2S applications (where the steel is HIC tested).
Masteel UK Limited stock ASTM A516 Grade 65 carbon steel plates which come with mill certification in compliance with EN10204 3.1 or EN10204 3.2. The plates are hard stamped and are fully traceable.
Table 2: Mechanical Properties of ASTM A516 Grade 65
Description | Grade 65 |
---|---|
Tensile strength (ksi) | 65-85 |
Tensile strength (MPa) | 450-585 |
Yield strength (ksi) | 35 |
Yield strength (MPa) | 240 |
Elongation in 200mm (min)(%) | 19 |
Elongation in 50mm (min) (%) | 21 |
Thickness (max)(mm) | 205 |
(Minimum values unless stated otherwise)
(Please note: the technical information above is for guidance only – for exact specifications please check with our Sales Team)
Table 1: Chemical Composition of ASTM A516 Grade 65
Carbon (C) | % |
12.5mm or less 12.5 - 50mm 50 - 100mm 100 - 200mm > 200mm | 0.24 0.26 0.28 0.29 0.29 |
Manganese (Mn) | % |
12.5mm or less • Heat Analysis : • Product Analysis : Over 12.5mm • Heat Analysis : • Product Analysis : | 0.85-1.20 0.79-1.30 0.85-1.20 0.79-1.30 |
Phosphorus (P) | % |
(max) | 0.035 |
Sulphur (S) | % |
(max) | 0.035 |
Silicon (Si) | % |
• Heat Analysis : • Product Analysis : | 0.15-0.40 0.13-0.45 |
(Maximum values unless stated otherwise)